NOMINAL DATA SHEET
| CHEMICAL COMPOSITION |
MECHANICAL PROPERTIES
(ANNEALED CONDITION) |
|
| C - 0.08max |
Ultimate Tensile Strength psi -
95,000 |
| Si - 1.00max |
0.2% Offset Yield Strength psi -
40,000 |
| Mn - 2.00max |
Percent Elongation in 2 inches - 50 |
| P - 0.045max |
Hardness Rockwell - B80 |
| S - 0.030max |
|
| Cr - 18-20 |
|
| Ni - 8-10.50 |
|
| |
|
PHYSICAL PROPERTIES(ANNEALED CONDITION)
Modulus of Elasticity in tension psi - 28.0 x 10(******)
Density(lbs./cu.in) - 0.29
Electrical Resistivity at room temp.(microhm-cm) - 72
Mean Coefficient of Thermal Expansion
in./in./ F(32-212 F) - 9.6 x 10(-******)
(******) = to the 6
(-******) = to the minus 6 |
Top of Page
NOMINAL DATA SHEET
| CHEMICAL COMPOSITION |
MECHANICAL PROPERTIES
(ANNEALED CONDITION) |
|
| C - 0.03max |
Ultimate Tensile Strength psi -
90,000 |
| Si - 1.00max |
0.2% Offset Yield Strength psi -
40,000 |
| Mn - 2.00max |
Percent Elongation in 2 inches - 50 |
| P - 0.045max |
Hardness Rockwell - B80 |
| S - 0.030max |
|
| Cr - 18-20 |
|
| Ni - 8-12 |
|
| |
PHYSICAL PROPERTIES(ANNEALED CONDITION)
Modulus of Elasticity in tension psi - 28.0 x 10(******)
Density(lbs./cu.in) - 0.29
Electrical Resistivity at room temp.(microhm-cm) - 72
Mean Coefficient of Thermal Expansion
in./in./ F(32-212 F) - 9.6 x 10(-******)
(******) = to the 6
(-******) = to the minus 6 |
Top of Page
NOMINAL DATA SHEET
| CHEMICAL COMPOSITION |
MECHANICAL PROPERTIES
(ANNEALED CONDITION) |
|
| C - 0.08max |
Ultimate Tensile Strength psi -
90,000 |
| Si - 1.00max |
0.2% Offset Yield Strength psi -
40,000 |
| Mn - 2.00max |
Percent Elongation in 2 inches - 50 |
| P - 0.045max |
Hardness Rockwell - B80 |
| S - 0.030max |
|
| Cr - 16-18 |
|
| Ni - 10-14 |
|
| Mo - 2-3 |
|
| |
PHYSICAL PROPERTIES(ANNEALED CONDITION)
Modulus of Elasticity in tension psi - 28.0 x 10(******)
Density(lbs./cu.in) - 0.29
Electrical Resistivity at room temp.(microhm-cm) - 74
Mean Coefficient of Thermal Expansion
in./in./ F(32-212 F) - 8.9 x 10(-******)
(******) = to the 6
(-******) = to the minus 6 |
Top of Page
NOMINAL DATA SHEET
| CHEMICAL COMPOSITION |
MECHANICAL PROPERTIES
(ANNEALED CONDITION) |
|
| C - 0.03max |
Ultimate Tensile Strength psi -
90,000 |
| Si - 1.00max |
0.2% Offset Yield Strength psi -
40,000 |
| Mn - 2.00max |
Percent Elongation in 2 inches - 50 |
| P - 0.045max |
Hardness Rockwell - B80 |
| S - 0.030max |
|
| Cr - 16-18 |
|
| Ni - 10-14 |
|
| Mo - 2-3 |
|
| |
Top of Page
PHYSICAL PROPERTIES(ANNEALED CONDITION)
Modulus of Elasticity in tension psi - 28.0 x 10(******)
Density(lbs./cu.in) - 0.29
Electrical Resistivity at room temp.(microhm-cm) - 74
Mean Coefficient of Thermal Expansion in./in./ F(32-212 F) - 8.9 x
10(-******)
(******) = to the 6
(-******) = to the minus 6 |
|
Available Sizes |
ROD
|
COIL/
FOIL
|
|
|
.125
.250
.312
.437
.500
.625
.750
.875
1.00
1.25
1.50
1.75
2.00
3.00
4.00
5.00
6.00
7.00
8.00
9.00
10.0
11.0
12.0
13.0
14.0
15.0
16.0
|
.001
.002
.003
.004
.005
.010
.015
.020
.030
.040
.050
.062
|
|
.050
.062
.078
.109
.125
.140
|
*NOTE: Other sizes available upon request.
Top of Page
Disclaimer
Every effort is made to ensure that
technical specifications are accurate. However, technical specifications
included herein should be used as a guideline only. All specifications are
subject to change without notice.
|