AVAILABLE SIZES
NOMINAL DATA SHEET
|
TYPICAL CHEMISTRY
|
| MOLYBDENUM |
99.9%(minimum) |
| POTASSIUM |
.0007 |
| ALUMINUM |
.0005 |
| SILICON |
.0050 |
| IRON |
.0040 |
| NICKEL |
.0030 |
| COPPER |
.0001 |
| CHROMIUM |
.0001 |
| SODIUM |
.0001 |
| TUNGSTEN |
.0020 |
|
|
Top of Page
|
TYPICAL PROPERTIES
|
| ATOMIC WEIGHT |
95.94 |
|
|
| DENSITY |
10.14 gm/cm3 |
|
|
| MELTING POINT |
2610 +/- 10 C |
THERMAL
CONDUCTIVITY |
| RECRYSTALLIZATION |
|
20 C |
0.34 cal/cm/s/ C |
| TEMPERATURE(100%) |
|
1000 C |
0.25 cal/cm/s/ C |
| RECRYSTALLIZATION |
1000 to 1100 C |
1500 C |
0.22 cal/cm/s/
C |
| |
|
2200 C |
0.17 cal/cm/s/ C |
| TRANSITION
POINT |
|
|
| BRITTLE/DUCTILE |
-100 to 100 C |
SPECIFIC
HEAT |
| |
|
20 C |
6.2 x 10-2 cal/gm/ C |
| VAPOR
PRESSURE |
1000 C |
7.4 x 10-2 cal/gm/ C |
| 1500 C |
6.4 x 10-9 mm
Hg |
2000 C |
10.0 x 10-2
cal/gm/ C |
| 2000 C |
4.0 x 10-5 mm Hg |
|
|
| 2500 C |
1.0 x 10-2 mm Hg |
RESTIVITY |
| |
|
20 C |
5.3 x 10-6 ohm-cm |
| COEFFICIENT
OF |
1000 C |
3.2 x 10-5
ohm-cm |
| LINEAR
EXPANSION |
2000 C |
6.1 x 10-5 ohm-cm |
| 20 C |
5.3 x 10-6 C-1 |
|
|
| 20-1000 C |
5.8 x 10-6 C-1 |
TEMPERATURE
COEFFICIENT |
| 20-1500 C |
6.5 x 10-6 C-1 |
OF THE
RESTIVITY |
| |
|
(20-100 C) |
4.5 x 10-3 C-1 |
| TENSILE
STRENGTH |
|
|
| SHEET |
50 kpsi - 115 kpsi |
HARDNESS |
| ROD |
60 kpsi - 110
kpsi |
SHEET |
220 - 240 DPH |
| WIRE |
90 kpsi - 350
kpsi |
ROD |
200 - 220 DPH |
| |
|
WIRE |
250 - 300 DPH |
| YIELD
STRENGTH |
|
|
| (0.2% OFFSET) |
|
|
|
| SHEET |
40 kpsi - 95
kpsi |
|
|
| ROD 55 |
kpsi - 90 kpsi |
|
|
| WIRE |
75 kpsi - 300
kpsi |
|
|
| |
Top of Page
|
AVAILABLE
SIZES |
| SHEET |
PLATE |
COIL/FOIL |
ROD |
.050
.062
.078
.109
.125
.140 |
.250
.375
.500
.750
1.00 |
.003
.004
.005
.010
.015
.020
.030
.040
.050
.062 |
.125
.250
.312
.437
.500
.625
.750
.875
1.00
1.25
1.50
1.75
2.00
2.25
2.50
3.00
3.50
4.00 |
NOTE: Other sizes available upon request.
Get Quotation:
Sales
Solicite un
Precio
Top of Page
Disclaimer
Every effort is made to ensure that
technical specifications are accurate. However, technical specifications
included herein should be used as a guideline only. All specifications are
subject to change without notice.
|